PHYSICAL PROPERTIES
|
TEST METHODS
|
AVERAGE RESULTS
|
| Thickness |
ASTM D 1000
Substrate
Adhesive
Total (excluding liner)
Liner |
0.0033 inch (0.084mm)
0.0010 inch (0.025 mm)
0.0043 inch (0.109 mm)
0.0020 inch (0.051 mm)
|
Adhesion to:
-Polycarbonate |
PSTC-1
20 minute dwell
24 hour dwell |
5 oz/in (5.5 N/100 mm)
10 oz/in (10.9 N/100 mm)
|
| Tack |
ASTM D 2979
Polyken™ Probe Tack
1 second dwell, 1 cm/second speed |
200g
|
| Drop Shear |
PSTC-7 (except use 1/2" x 1" sample) |
> 100 hours
|
| Application Temperature |
Lowest application temperature to stainless steel |
50°F (10°C)
|
The following testing is performed with the B-282 printed with Brady R4300 ribbon using a BradyPrinter™ 300X thermal transfer printer. All samples were allowed to dwell 24 hours prior to testing. Samples were tested on flat aluminum panels.
|
PERFORMANCE PROPERTIES
|
TEST METHODS
|
TYPICAL RESULTS
|
| High Service Temperature |
30 days at 176°F (80°C) |
No visible effect to tape or printing. |
| Low Service Temperature |
30 days at -40°F (-40°C) |
No visible effect to tape or printing. |
| Humidity Resistance |
30 days at 122ºF (50°C), 95% R.H. |
No visible effect to tape or printing. |
| UV Light Resistance |
30 days in UV Sunlighter™ 100 |
No visible effect to tape or printing. |
| Weatherability |
30 days in Xenon Arc Weatherometer |
No visible effect to tape or printing. |
Pro duct testing supports a customer performance expectation of at least six months from the date of receipt for this product as long as this product is stored in its original packaging in an environment below 80
° F and 60% R.H.